项 目 \ 牌 号
|
烧结莫来石砖
|
刚玉莫来石砖
|
刚玉砖
|
莫来石硅线石砖
|
莫来石堇青石砖
|
MZ-60
|
MZ-65
|
MZ-70
|
MZ-75
|
GMS-80
|
GMS-85
|
GY-90Z
|
GY-92Z
|
GY-98
|
MGS-65
|
MGS-70
|
MJS-40
|
Al2O3 % |
≥60 |
≥65 |
≥70 |
≥75 |
≥80 |
≥85 |
≥90 |
≥94 |
≥98 |
≥65
|
≥70
|
≥40
|
Fe2O3 % |
≤1.2 |
≤1.0 |
≤0.8 |
≤0.6 |
≤0.5 |
≤0.5 |
≤1.0 |
≤1.0 |
≤0.3 |
|
|
|
耐火度 ℃
|
>1790 |
>1790 |
>1790 |
>1790 |
>1790 |
>1790 |
>1790 |
>1790 |
>1790 |
>1790
|
>1790
|
|
体积密度 g/cm3 |
≥2.45 |
≥2.50 |
≥2.55 |
≥2.60 |
≥2.65 |
≥2.75 |
≥2.95 |
≥3.1 |
≥3.1 |
|
|
|
显气孔率 %
|
≤20 |
≤20 |
≤20 |
≤20 |
≤20 |
≤20 |
≤16 |
≤16 |
≤20 |
≤22 |
≤20 |
≤28
|
常温耐压强度 MPa |
≥50 |
≥50 |
≥55 |
≥60 |
≥60 |
≥60 |
≥80 |
≥80 |
≥60 |
≥50 |
≥60 |
≥35
|
荷重软化温度 T2 ℃ |
≥1600 |
≥1650 |
≥1700 |
≥1700 |
≥1700 |
≥1700 |
≥1620 |
≥1650 |
≥1700 |
≥1600 |
≥1650 |
|
重烧线变化率 %
1500℃×3h |
±0.1 |
±0.1 |
±0.1 |
±0.1 |
±0.2 |
±0.2 |
±0.2 |
|
±0.1 |
±0.2 |
±0.1 |
|
热震稳定性,次(1100℃ 水冷) |
|
|
|
|
|
|
|
|
|
≥30 |
≥30 |
≥20 |
用 途 |
适用于各种高温窑炉及热工设备内壁、拱顶、燃烧室及工具砖等
|
|
|